X6Cr17 Stainless Steel Features
- Good corrosion resistance
- Versatile material
- Good formability
- Good oxidation resistance
- Magnetic
- Good creep resistance
- Cost-effective stainless steel grade
X6Cr17 Stainless Steel Manufacturer in China
X6Cr17 is a popular grade ferritic stainless steel. Elements present in this grade include carbon, manganese, and silicon. It has low carbon content which improves its welding characteristics. While manganese and silicon help to enhance their strength and toughness. X6Cr17 stainless steel has a relatively low thermal expansion coefficient. Thus, it is resistant to thermal distortion during heat treatment.
At Tuolian, we can easily form, weld, and machine stainless steel to suit various applications. We supply X6Cr17 in a wide range of sizes and thicknesses. You can request a range of forms such as plates, sheets, bars, tubes, etc.
If you have specific requirements, contact us immediately!
Wide Applications
- Pharmaceutical equipment
- Chemical processing equipment
- Petrochemical applications
- Automotive exhaust systems
- Food processing equipment
- Heat exchanger component
- Pulp and paper processing
- Oil and gas processing
- Architectural applications
- Aircraft components
- Industrial machinery component
Mechanical Properties
| Property | Value |
| Density | 7.7 g/cm3 |
| Modulus of Elasticity | 200 GPa |
| Poisson’s Ratio | 0.27-0.30 |
| Hardness, Brinell (@20°C) | 160-210 HB |
| Hardness, Rockwell B (@20°C) | 82-86 HRB |
| Tensile Strength, Ultimate (@20°C) | 480 MPa |
| Tensile Strength, Yield (@20°C) | 260 MPa |
| Elongation at Break (@20°C) | 25% |
| Reduction of Area | 45% |
Chemical Composition
| Element | Content (% by weight) |
| Carbon (C) | 0.08 max |
| Silicon (Si) | 1.00 max |
| Manganese (Mn) | 1.50 max |
| Phosphorus (P) | 0.040 max |
| Sulfur (S) | 0.015 max |
| Chromium (Cr) | 16.00-18.00 |
| Iron (Fe) | Balance |
Equivalent Grades
| Country/Region | Standard | Equivalent Grades |
| European Union | EN 10088-1 | X6Cr17, 1.4016 |
| Germany | DIN 17440 | X6Cr17, X 6 Cr 17, 1.4016 |
| United States | ASTM A240 | S41000 |
| Japan | JIS G4304 | SUS410 |
| China | GB/T 3280 | 1Cr13 |
- Strength Properties at Elevated Temperatures
- Standard
- Electrical Properties
| Temperature (°C) | Yield Strength (MPa) | Tensile Strength (MPa) |
| 20 | 260 | 480 |
| 100 | 220 | 450 |
| 200 | 200 | 440 |
| 300 | 185 | 420 |
| 400 | 170 | 400 |
| 500 | 150 | 380 |
| 600 | 130 | 360 |
| 700 | 110 | 340 |
| 800 | 95 | 320 |
| Standard | Country |
| EN 10088-1 | European Union |
| DIN 17440 | Germany |
| ASTM A240 | United States |
| JIS G4304 | Japan |
| GB/T 3280 | China |
| Property | Value |
| Electrical conductivity (at 20°C) | 2.35 × 10^6 S/m |
| Electrical resistivity (at 20°C) | 0.42 μΩ·m |
| Dielectric constant (at 1 MHz) | 2.1 |
| Dielectric strength (at 20°C) | 20 kV/mm |